ORACLE (TM) 5015G is an impact-modified, 15% glass fiber reinforced injection molding grade PA6 , developed for applications requiring improved toughness in combination with a balance of strength, stiffness, excellent moldability and surface aesthetics.
| TEST ITEMS | TEST METHOD AND CONDITIONS | TEST RESULTS | ||
| TEST METHOD | UNIT | CONTITIONS | ||
| (DRY)23 | ||||
| Density | ISO1183 | g/cm3 | 1.36 | |
| Melt Volume Rate | ISO1133 | cc/10min | 250-2.16kg | 20.4 |
| Tensile Strengh | ISO527 | MPa | 10m/min | 125 |
| Tensile Modulus | ISO527 | MPa | 5,800 | |
| Tensile strain at break | ISO527 | % | 5 | |
| Flexural Strength | ISO178 | MPa | 2m/min | 162 |
| Flexural Modulus | ISO178 | MPa | 5,400 | |
| Charpy Notched | ISO179 | KJ/m2 | 2.9m/s-1J | 8 |
| Izod Notched Impact | ISO180 | KJ/m2 | 3.5m/s-1J | 7 |
| Flame resistance | UL-94 | HB | ||
| Ash content | % | 15.2 | ||
| Processing Guidelines | ||||
| Material HandlingProduct is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 2-4 hours is generally sufficient | ||||
| Typical ProfileMelt Temperature 250-280 °CMold Temperature 60-90 °CInjection and Packing Pressure 35-125 bar (500-1500 psi) | ||||
| Fill RateFast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate. | ||||
Polyamide 6 - 15%GF