Grade 304 stainless steel strip
Standard: JIS, AISI, ASTM, GB, DIN, EN
Thickness: 0.3mm---25mm
Width:50mm---1500mm
Grade 304 stainless steel strip
| |
| thickness | Thickness allow deviation | 10~150 | 150~300 | 300~≤450 | 0.03~0.10 | ±0.005 | ±0.005 | ±0.010 | 0.10~0.15 | ±0.010 | ±0.010 | ±0.010 | 0.15~0.25 | +0.010-0.015 | +0.010-0.015 | +0.010-0.015 | 0.25~0.45 | ±0.015 | ±0.015 | ±0.015 | 0.45~0.65 | ±0.020 | ±0.020 | ±0.020 | 0.65~0.90 | +0.025-0.030 | +0.025-0.030 | ±0.030 | 0.90~1.20 | +0.030-0.035 | ±0.035 | ±0.040 | 1.20~1.50 | +0.040-0.045 | +0.040-0.045 | ±0.050 |
| Width deviation | 5~150 | 150~300 | 300~≤450 | 0.03~0.15 | ±0.10 | ±0.10 | ±0.20 | 0.15~0.50 | ±0.15 | ±0.15 | ±0.20 | 0.50~1.00 | ±0.20 | ±0.20 | ±0.25 | 1.00~1.50 | ±0.20 | ±0.25 | ±0.25 |
|
| Chemical Composition of Stainless Steel 304 |
Table 1. Typical chemical composition for 304 stainless steel alloys % | 304 | 304L | 304H | C | 0-0.07 | 0-0.03 | 0.04-1 | Mn | 0-2.0 | 0-2.0 | 0-2.0 | Si | 0-1 | 0-1 | 0-1 | P | 0-0.05 | 0-0.05 | 0-0.05 | S | 0-0.02 | 0-0.02 | 0-0.02 | Cr | 17.5-19.5 | 17.5-19.5 | 17.5-19.5 | Ni | 8-10.5 | 8-10.5 | 8-10.5 | Fe | Balance | Balance | Balance |
|
| Properties of Stainless Steel 304 |
| Mechanical Properties of Stainless Steel 304 Table 2. Typical mechanical properties for 304 stainless steel alloys Grade | 304 | 304L | 304H | Tensile Strength (MPa) | 520-720 | 500-6070 | 520-720 | Compression Strength (MPa) | 210 | - | - | Proof Stress 0.2% (MPa) | 210 | 200 | 210 | Elongation A5 (%) | 45 Min | 45 Min | 40 Min | Hardness Rockwell B | 92 | - | - |
Physical Properties of Stainless Steel 304Table 3. Typical physical properties for 304 stainless steel alloys Property | Value | Density | 8.00 g/cm3 | Melting Point | 1450°C | Modulus of Elasticity | 193 GPa | Electrical Resistivity | 0.072x10-6 Ù.m | Thermal Conductivity | 16.2 W/m.K | Thermal Expansion | 17.2x10-6 /K |
|