1,For our PVC compound products, PVC resin is the main raw material. And adding plasticizer, stabilizer, colorants and other additives , processed by mixing ,extruding and granulating. We have advanced technology, good plasitcization and stable performance. Our products mainly used for the elevator, electric welding machine, driving and outdoor portable electric wire and cable security lay
2,Use and standard: meet enterprises standard Q / 320287 NMM01-2008, used for elevator, electric welding machine, driving and outdoor portable electric wire and cable, conform to the corresponding cable specification.
3,Process: extrusion and injection
4,Appearance: cylindrical particles, plastication should be good, the color and luster is even, without obvious impurity.
5,Packing: 25kg net weight per in a kraft bag with insider PE bag
6,Transportation and storage: this kind of product in the transportation should not be weathered, should be stored in a clean, cool, dry and ventilated warehouse , storage period is from the date for a year.
We will also produce the products according with customer's requirement, For example, Flame-resisting compounds, Low temperature resisting compounds, Heat-resistant compounds, and low smoke low halogen compounds, Transparent PVC compounds etc.Our products can fit the ROHS directive, REACH,non-PAHS, ,ASTM standard and etc.
PVC COMPOUND SPECIFICATION
Description index | TYPE | |||||||
J-70 | JR-70 | H-70 | HR-70 | JGD-70 | HI-90 | HII-90 | J-90 | |
TensileStrength(before ageing) / MPa ≥ | 15.0 | 15.0 | 15.0 | 12.5 | 16.0 | 16.0 | 16.0 | 16.0 |
Elongation at rupture (before ageing) / %> | 150 | 180 | 180 | 200 | 150 | 180 | 180 | 150 |
TensileStrength (after ageing) / Mpa ≥ | 15.0 | 15.0 | 15.0 | 12.5 | 16.0 | 16.0 | 16.0 | 16.0 |
Elongation at rupture (after ageing) / % > | 150 | 180 | 180 | 200 | 150 | 180 | 180 | 150 |
Thermal Stability (at 200 °C) / min ≥ | 60 | 50 | 50 | 65 | 100 | 80 | 180 | 180 |
Volume electric resistance (at 20°C)≥ | 1.0*1012 | 1.0*1011 | 1.0*108 | 1.0*108 | 3.0*1012 | 1.0*109 | 1.0*109 | 1.0*1012 |
Volume electric resistance (at working temperature) / m≥ | 70 °C | 70 °C | - | - | 70 °C | - | - | 95 °C |
1.0*109 | 1.0*109 | - | - | 5.0*109 | - | - | 5.0*108 | |
Loss of Mass (at 100 °C) / g/m2 ≤ | 168h | 168h | 168h | 168h | 168h | 240h | 240h | 240h |
20 | 20 | 23 | 25 | 20 | 15 | 20 | 20 | |
Fragility temperature°C | -15 | -20 | -25 | -30 | -15 | -20 | -20 | -15 |
Colour Shade | SHALL MATCH | |||||||