ZIRCONIA CERAMIC RING FOR PAD PRINTER APPLICATION
COLOR: WHITE
TYPES: BORE DIAMETER FROM 20-250MM, SINGLE/DOUBLE BLADE
APPLICATION: PAD PRINTER AND RELEVANT INDUSTRY DOMAIN
Item | Unit | ZrO2 |
Desity | g/cm3 | 6.05 |
Poisson Ratio | 0.3 | |
Hardness (HV) | 1200 | |
Hardness(HRC) | 70 | |
Modulus of Elaslicity | Gpa | 210 |
Thermal Expansion Coefficent | 10-6K-1 | 10.5 |
Thermal Conductivity(500°C) | W/mK | 2 |
Bending Strength(800°C) | Mpa | 300 |
Crushing Strength(800°C) | Mpa | 2100 |
Fracture Toughness | MPa1/2 | 10 |
Specific Conductivity(600°C) | Ωmm2/m | 1015 |
Max Useage Temperature | °C | 550 |
Corrosion Resistance | Better | |
Fatigue Stress Recycles(50% Fail) | Times | 105 |
Dimension Stablillty with Temperature | - | |
Centrifugal Force | large | |
Non-lubrication Friction | Little | |
Magnetism | Naught | |
Failure Mode under Rolling Contact | Smash |