Description: titanium target
Grade: 2
Size: Dia 100 x 32 mm
Application: Sputtering and Coating
A & V: ISO 9001: 2008
Packing: Export wooden case lined with foam or at buyer's option
Titanium Grade 2 is a pure titanium offering an excellent balance of strength and ductility. The material has good toughness and is readily weldable. It is corrosion resistant in highly oxidizing and middly reducing environments, castable and often utilized in cast valves and fittings.
Mechanical Properties of CP GR2 | |||||
| Guaranteed Room Temperature Minimum | Typical Strength (%RT) & Ductility 200F 400 F 600F 800F 1000F | |||
Ultimate Tensile Strength, psi | 50,000 | 80 57 46 36 28 | |||
Yield Strength, 0.2% Offset, psi | 40,000 | 76 46 30 26 20 | |||
El in 2"(>0.025" thick), pct | 22 | 42 37 25 31 | |||
Reduction of Area, Percent | 35 | 57 76 76 75 | |||
Bend Radius | 2T 2.5T |
| |||
Weld Bend Radius | Approx. 3-4T |
| |||
Hardness | Brinell 200 |
| |||
Physical Properties for CP GR2 | |||||
Modulus of Elasticity, psi(10^6) Tension | 14.9 | ||||
Modulus of Elasticity, psi(10^6) Torsion | Approximately 6.5 | ||||
Density, lb/ cu Inch | 0.163 | ||||
Melting Range, Deg. F | 3000 - 3100F | ||||
Specific Electrical Resistivity micro ohms/cm/sq cm | 56 | ||||
Specific Heat, Btu/lb/Deg. F | 0.125 at room temperature | ||||
Thermal Conductivity, Btu/hr.Ft^2 - Deg. F/ft | Approx. 9.5 at room temp. | ||||
Mean Coefficient of Thermal Expansion Per F (10^6)32-212F32-600F32-1000F32-1200F32-1500F | 4.85.15.45.65.6 | ||||
Oxidation Characteristics in Air | 400 F 600 F 800 F 1000F | ||||
Short Time | Good Good Good Moderate | ||||
Long Term | Good Good Slight Moderate | ||||
Remarks on Fabrication for CP GR2 | |||||
Beta Transus | 1650 - 1700 | ||||
Cutting | Readily cut with saw or abrasive wheel | ||||
Machining | Rigid set-up, medium speed, heavy feed, sharp tools, adequate coolant | ||||
Forming | Readily formable at room temp. Complex shapes require heat | ||||
Joining, Welding | Complex weldable, fusion welding requires protection | ||||
Remarks on Heat Treatment for CP GR2 & CP GR4 | |||||
Initial Forging | Approx. 1650F rough breakdown finish 1550F | ||||
Annealing | 1300F, 2hr, air cool | ||||
Solution Treating | Not applicable | ||||
Aging | Not applicable | ||||
Stress Relief Annealing | 900 - 1000F, 45 min. | ||||
Other Technical Data for CP GR2 | |||||
Principal Uses | Airframe applications, skins, chemical industry, applications where maximum formability required with moderate strength. | ||||
Available Forms | Sheet, strip, plate, bar, billet, wire, tubing, extrusions. | ||||
Nominal Composition | 0.08% max C, 0.05% max N, 0.015% max H (sheet), 0.20% max Fe. | ||||
Type Structure | Alpha | ||||
titanium target