Fluorinated Ethylene-propylene Shrinkable Sleeve
FEP heat-shrinkable sleeve is made from FEP resin and is prepared by the technology of extrusion and blowing. FEP heat-shrinkable sleeve has a high UV transmission, UV resistance and good electric property. The shrinkage temperature is from 130200. The shrinkage rate is about 30%. Another major advantage of FEP heat-shrinkable sleeve is being heat-sealed or welded to itself. So, FEP heat-shrinkable sleeve can be used as cable jackets, non-stick rollers, sensor probe covers, hose protection, electrical terminal insulation etc. It conforms to the enterprise standard of Q/GHAD 59-2006...........................................................
Main Properties
Item | Value | |
Tensile Strength MPa ≥ | 20 | |
Elongation @ Break % ≥ | 150 | |
Dielectric Strength (KV/mm) ≥ | Wall Thickness after shrinkage≤0.3mm | 10 |
0.3mmWall Thickness after shrinkage≤0.4mm | 11 | |
Wall Thickness after shrinkage0.4mm | 12 | |
Specification
Code | I.D. | Wall Thickness after shrinkage | Continues Length | |
Min.(Before Shrinkage) | Max.(After Shrinkage) | Wall Thickness & Tolerance | ||
FEP-G-S-1 | 6.5 | 5 | 0.20±0.08 0.25±0.08 0.30±0.08 0.40±0.08 0.5±0.10 0.6±0.15 0.7±0.15 | ≥500 |
FEP-G-S-2 | 8 | 6 | ≥500 | |
FEP-G-S-3 | 9 | 7 | ≥500 | |
FEP-G-S-4 | 10 | 8 | ≥500 | |
FEP-G-S-5 | 12 | 9 | ≥500 | |
FEP-G-S-6 | 14 | 10.5 | ≥500 | |
FEP-G-S-7 | 15 | 11 | ≥500 | |
FEP-G-S-8 | 16 | 12 | ≥500 | |
FEP-G-S-9 | 18 | 13.5 | ≥500 | |
FEP-G-S-10 | 22 | 16 | ≥500 | |
FEP-G-S-11 | 24 | 18 | ≥500 | |
FEP-G-S-12 | 26 | 20 | ≥500 | |
FEP-G-S-13 | 29 | 22 | ≥500 | |
FEP-G-S-14 | 32 | 25 | ≥500 | |
FEP-G-S-15 | 38 | 30 | ≥500 | |
FEP-G-S-16 | 41 | 32 | ≥500 | |
FEP-G-S-17 | 45 | 35 | ≥500 | |
FEP-G-S-18 | 50 | 38 | ≥500 | |
FEP-G-S-19 | 52 | 40 | ≥500 | |
FEP-G-S-20 | 60 | 45 | ≥500 | |
FEP-G-S-21 | 72 | 55 | ≥500 | |
FEP-G-S-22 | 90 | 70 | ≥500 | |
FEP-G-S-23 | 115 | 90 | ≥500 | |
FEP-G-S-24 | 130 | 110 | ≥500 | |
FEP-G-S-25 | 140 | 120 | ≥500 | |
Note: Customers request negotiable | ||||