| Co | weight | ||||||||||
| Grade | losing | Hall flow | Bulk density | HC | Magnetic Saturation | Density | Hardness | Bending Strength | Porosity | Equivalent | |
| coefficient | (S/50g) | (g/cm3) | Coercive Force | (%) | (g/cm3) | (HRA) | (N/mm2) | ≤ | ISO Grade | ||
| (kA/m) | |||||||||||
| YG6x | 6 | 2.5-3.0 | 27 | 3.20-3.30 | 19.0-21.0 | 90-98 | 14.85-15.0 | 91.5-93.0 | 2200 | A02B00C00 | K10 |
| YG6 | 6 | 2.5-3.0 | 28 | 3.30-3.50 | 12.5-17.0 | 90-98 | 14.85-15.00 | 90.5-92.0 | 2050 | A02B00C00 | K20 |
| YG8 | 8 | 2.5-3.0 | 28 | 3.20-3.50 | 10.0-15.0 | 90-98 | 14.65-14.85 | 89.5-91.0 | 2200 | A02B00C00 | K30 |
| YG10 | 10 | 2.5-3.0 | 31 | 3.05-3.20 | 8.0-11.0 | 90-98 | 14.40-14.65 | 88.0-89.0 | 2450 | A02B00C00 | K40 |
| YG10C | 10.4 | 2.5-3.0 | 26 | 3.20-3.40 | 6.00-8.00 | 91-98 | 14.50-14.75 | 86.0-87.0 | 2500 | A02B00C00 | |
| 15.1 | 2.5-3.0 | 27 | 3.10-3.20 | ||||||||
| YG15C | 5.50-7.50 | 90-96 | 13.50-13.70 | 84.0-86.0 | 2200 | A02B00C00 | |||||
| YT5 | 9 | 2.5-3.0 | 31 | 2.90-3.10 | 8.5-12.5 | 94-100 | 12.85-13.05 | 89.5-91.0 | 1750 | A02B02C00 | P30 |
| YT15 | 6 | 2.5-3.0 | 32 | 2.65-3.0 | 11.0-13.0 | 94-100 | 11.25-11.50 | 92.0-93.0 | 1850 | A02B02C00 | P15 |
| YT14 | 8 | 2.5-3.0 | 32 | 2.60-2.90 | 10.0-14.0 | 94-100 | 11.35-11.60 | 91.5-92.5 | 1750 | A02B02C00 | P15 |
| YW1 | 6 | 2.5-3.0 | 30 | 2.90-3.10 | 18.5-22.0 | 80-95 | 13.5-13.7 | 92-93.5 | 1500 | A02B02C00 | M10 |
| YW2 | 8 | 2.5-3.0 | 30 | 2.90-3.10 | 14.0-17.0 | 85-95 | 13.35-13.55 | 91.5-92.5 | 1600 | A02B02C00 | M20 |
Tungsten Carbide Powder