Low levels of C & O along with good compressibility. Higher density compacts with Excelent mechanical properties.

This is the workhorse of our atomized powders; the material that has advanced P/M into the modern age of higher density compacts. More P/M components have MF200.30 as their base than any other atomized powder. It has low levels of carbon and oxygen along with good compressiblity.

With small additions of graphite, copper, or nickel, MF200.30 provides excellent mechanical properties.

MF200.30 is also used extensively for electromagnetic applications.

Description of Article:  Water Atomized Iron Powder 

Grade: MF200.30   Batch No. 

Executive Standard: QB/MX-2009

Chemical Content wt%	Test Result wt%	Standard wt%
C	0.0020	≤0.015
Si	0.040	≤0.05
Mn	0.12	≤0.15
P	0.011	≤0.015
S	0.024	≤0.025
Hydrogen Loss	0.18	≤0.25
TFe	99.16	>98.5
Physical Properties	Test Result	Standard
Apparent Density(g/cm3)	3.04	3.00±0.10
Flow Rate (s/50g)	28.77	≤30
Compressibility (600MPa) g/cm3	7.09	≥7.05
Screen Analysis wt%
>180μm(+80mesh)	0.81	≤1.0
180-150μm (-80~+100mesh)	7.18	≤10
150-100μm (-100~+150mesh)	24.81	20-35
100-63μm (-150~+230mesh)	27.08	20-40
<63μm(-230mesh)	39.98	≥25

Atomized Iron Powder