It is widely used in low temperature cold areas, the effect of deicing or snow melting is significant.
Feature:1. It is widely used in low temperature cold areas, the effect of deicing or snow melting is significant.2. It is non-toxic, odorless, environmental pollution, but it can't be eaten.3. It is dampened easily without corrosion to the human health, animals or other objects.4. Water self-heating, without the manpower and resources, and other resources, is energy-efficient products.5. In addition to snow and ice at the same time on the tarmac and cement road to play a protective effect to prevent the ground cracks, and repair cracks on the ground.6. Water resulting from high fever, should be used to prevent spills burn and get protection. The state inspection reports of our snow melting agent :
| Sodium hloride | Calcium hloride | Magnesium hloride | This Snow-removing agent |
Corrosve action on metals | 100% | 50-70% | 40-60% | 5-10% |
2 | Freezing point °C | **** | -15 | **** |
3 | Cadmium % | ≤0.0005 | 0.00021 | Conform |
4 | Chromium % | ≤0.0015 | 0.00031 | Conform |
5 | Mercury % | ≤0.0001 | <0.0001 | Conform |
6 | Concrete corrosion rate % | ≤0.30 | 0 | Conform |
7 | The decay rate of road surface friction % | Wet basis≤16 | 11 | Conform |
8 | Lead % | ≤0.0025 | <0.0025 | Conform |
9 | Dissolution rate g/min | ≥6.0 | 6.3 | Conform |
10 | Deicing or snow melting capacity g/min | Sodium chloride snowmelt capacity 90% | 91 | Conform |
11 | Arsenic % | ≤0.0005 | <0.0005 | Conform |
12 | Carbon steel corrosion rate % | ≤0.18 | 0.004 | Conform |
13 | Exterior | Granules or flakes solid | White flaky solid | Conform |
Performance comparison between this product and other salt snow melting agents:
| Sodium hloride | Calcium hloride | Magnesium hloride | This Snow-removing agent |
Corrosve action on metals | 100% | 50-70% | 40-60% | 5-10% |
Corrosve action on cement (300 times frost thawing ) Corrosve action on cement (300 times frost thawing ) | 100% seriously destroyed | 250% seriously | 5% slightly destroyed | 1% Non-destroyed |
Effect on solis | Cause soli hardened | Slightly hardened | Small effect | Improving alkaline soli |
Effect on undergroud water | Sodium increases, adverse to human body,such as: hypertensionSodium increases, adverse to human body,such as: hypertension | Calcium increases,smaller impact on human body | Magnesium increases, benefit to human body | Magnesium increases, benefit to human body |
Lowest freezing point | -21°C | -50°C | -33°C | -80°C |
Snow melt speed | 100% 100% | 150% | 200% | 200% |
Appropriate working temperature | -1°C to -10°C | -1°C to -30°C | -1°C to -20°C | -1°C to -60°C |
Hold time ( Spray before snow) | 1 day | 1-2 days | 2-3 days | 6-10 days |
Snow-removing and snow melting rates of comparison between this product and other salt snow melting agents:
| Sodium hloride | Calcium hloride | Magnesium hloride | This Snow removing agent |
Temperature | -20 | -20 | -20 | -20 |
Snow melting ( min ) | 190 | 85 | 92 | 2 |
Application: roads, mountain roads, bridges, structures surface, Yunnan and Guizhou,etc. as well as general civil.Specifications: powder or granular.Packing: waterproof packing, 25kg / bag or customized packaging accordingto customer requirements.Application method: both artificial dispersal or machine spreading, thisproduct can also be dissolved into a solution of different concentrations weresprayed. The use of snowmelt agent process, the user can speed according tosnowfall, ice thickness, temperature, traffic, etc. and flexibility grasp.Pre-spreading amount of snowmelt agent better.