Grinding Media(Forged Ball & Cast Ball)
1. High hardness
2. Good wear-resistance
3. High toughness
4. No mal-roundness
Grinding Media(Forged Ball & Cast Ball)
We are a professional manufacturer of grinding steel balls in Shandong,China. Our annual production capacity is about 80000MT. We own an integrated set of advanced import production line, so that you can be satisfied with the quality of our products.
Grinding media Applied Fields
1. Mines
2. Cement Plants
3. Chemical Industries
4. Power Stations
Type and Chemical Composition of Forged Ball
Name | Material | C | Mn | Si | Cr | S | P |
ZW-1 | 50Mn | 0.48-0.56 | 0.70-1.0 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
ZW-2 | 60Mn | 0.57-0.65 | 0.70-1.0 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
ZW-3 | 65Mn | 0.60-0.70 | 0.90-1.2 | 0.17-0.37 | ≤0.25 | ≤0.035 | ≤0.035 |
ZW-4 | B2 | 0.70-0.85 | 0.70-0.80 | 0.17-0.37 | 0.2-0.7 | ≤0.03 | ≤0.03 |
ZW-5 | 75SiMn | 0.70-0.90 | 0.70-1.20 | 0.4-0.8 | ≤0.25 | ≤0.03 | ≤0.03 |
ZW-6 | Wear-resistant Alloy | 0.50-0.65 | 0.4-1.0 | 1.4-1.8 | 0.9-1.2 | ≤0.03 | ≤0.03 |
Type and Chemical Composition of Cast Ball
NAME | BRAND | CHEMICAL COMPOSITION(%) |
C | Si | Mn | Cr | Mo | P | S |
High Chromium Cast Ball | ZQCr26 | 2.0-3.4 | ≤1.2 | ≤1.5 | 22-28 | ≤1.5 | ≤0.10 | ≤0.10 |
ZQCr20 | 2.0-3.4 | ≤1.2 | ≤1.5 | 17-22 | ≤1.5 | ≤0.10 | ≤0.10 |
ZQCr17 | 2.0-3.4 | ≤1.0 | ≤2.5 | 15-17 | ≤1.5 | ≤0.10 | ≤0.10 |
ZQCr13 | 1.7-3.4 | ≤1.0 | ≤2.5 | 11-14 | ≤1.5 | ≤0.10 | ≤0.10 |
Physical Property of Forged Ball
Name | Material | Impact Test(Ak.J/cm²) | Endurance Test Times(5m/T) | Surface Hardness (Φ25mm- Φ60mm) | Core Hardness (Φ25mm- Φ60mm) | Surface Hardness (Φ70mm- Φ100mm) | Core Hardness (Φ70mm- Φ100mm) | Breakage |
ZW-1 | 50Mn | ≥12 | ≥10000 | ≥56 | ≥35 | ≥56 | ≥28 | <1% |
ZW-2 | 60Mn | ≥13 | ≥10000 | ≥58 | ≥38 | ≥58 | ≥29 | <1% |
ZW-3 | 65Mn | ≥15 | ≥12000 | ≥60 | ≥42 | ≥60 | ≥30 | <1% |
ZW-4 | B2 | ≥17 | ≥12000 | ≥60 | ≥52 | ≥60 | ≥50 | <1% |
ZW-5 | 75SiMn | ≥16 | ≥12000 | ≥60 | ≥50 | ≥60 | ≥48 | <1% |
ZW-6 | Wear-resistant Alloy | ≥17 | ≥12000 | ≥60 | ≥54 | ≥60 | ≥52 | <1% |
Physical Propertof Casting Ball
MAME | BRAND | HARDNESS | IMPACT VALUE ak(J/cm2) | METALLOGRAPHIC ORGANIZATION | BALLS |
FATIGUE LIFE |
QUENCHING STATE(A) | NO- QUENCHING STATE(A) | IMPACT |
High Chromium Casting Ball | ZQCr26 | ≥60 | ≥45 | ≥4.0 | M+C | ≥8000 |
ZQCr20 | ≥60 | ≥45 | ≥3.5 | ≥8000 |
ZQCr17 | ≥60 | ≥49 | ≥3.0 | ≥8000 |
ZQCr13 | ≥60 | ≥50 | ≥2.3 | ≥8000 |
Grinding Media Packaging
Ton bags (1000Kg Per Bag)
Iron drums (850~920Kg Per Drum)
Grinding Media For Nikel Mining