Galvanized iron wire 1.Material is Q195(C is 0.06% ~ 0.12%) 2.Zinc coating is 40g/m2~330g/m2 3.Tensile strength is 400N-600N

Hot Dip Galvanized Iron Wire

Author: HeBei BoYang Hardware Wire Mesh Products Co.,Ltd.

Related products: galvanized iron wire, hot dip galvanized iron wire, electro galvanized iron wire, baling wire, binding wire, cut iron wire, u type wire, coil wire, round wire, flat wire

 

Process of Producing

1.before drawing, oxide skin of wire rod shoud be removed

 two ways of drawing: powder-drawing to draw thicker wire; water-drawing to draw thinner wire

2.annealing to reduce the T/S of the wire

3.acid-washing to remove the impurities on the surface  of the steel wire, preparing for the galvanized

   concentration of the HCl is 17%

4.feature of our electro galvanized wire: uniform galvanized, smooth surface

   feature of our hot dip galvanized wire: uneven galvanized, unsmooth surface

5.packaging is according to your requirements, general coil weight is 50kg, 100kg

 

 

AISI  Grade	Chemical Composition(%)
	C	Si	Mn	P	S	Ni	Cr	Mo
304	<=0.08	<=1.00	<=2.00	<=0.045	<=0.030	8.00~10.50	18.00~20.00	-
304H	>0.08	<=1.00	<=2.00	<=0.045	<=0.030	8.00~10.50	18.00~20.00	-
304L	<=0.030	<=1.00	<=2.00	<=0.045	<=0.030	9.00~13.50	18.00~20.00	-
316	<=0.045	<=1.00	<=2.00	<=0.045	<=0.030	10.00~14.00	10.00~18.00	2.00~3.00
316L	<=0.030	<=1.00	<=2.00	<=0.045	<=0.030	12.00~15.00	16.00~18.00	2.00~3.00
430	<=0.12	<=0.75	<=1.00	<=0.040	<=0.030	<=0.60	16.00~18.00	-
430A	<=0.06	<=0.50	<=0.50	<=0.030	<=0.50	<=0.25	14.00~17.00