APPLICATION
iron powder for metallurgy industry,for cored wire production
HSM80·240
Fe | Mn | Si | C | S | P | Hydrogen loss | Insolubles in HCL | Mo | Bulk density g/cm³ | ||||
Min ( wt%) | Max ( wt%) | ||||||||||||
98.00 | 0.40 | 0.15 | 0.07 | 0.030 | 0.030 | 0.50 | 0.40 | 2.302.50 | |||||
Fluidity | Copressibility | Size distribution (mesh) % | |||||||||||
+40 (>425 m) | -40+60 (250-425µ m) | -60+80 (180-250 µ m) | -80+100 (150-180 µ m) | -100+150 (106-150 µ m) | -150+200 (75-106 µ m) | -200 (<75 µ m) | -320 (<45 µ m) | ||||||
38 | 6.40 | ≤3 | Balance | Balance | Balance | Balance | 5-25 |
for welding electrode
HSM40·290
Fe | Mn | Si | C | S | P | Hydrogen loss | Insolubles in HCL | Mo | Bulk density g/cm³ | |||
Min ( wt%) | Max ( wt%) | |||||||||||
98.00 | 0.35 | 0.15 | 0.05 | 0.020 | 0.020 | 0.40 | — | — | 2.80~3.00 | |||
Fluidity | Copressibility | Size distribution (mesh) % | ||||||||||
+40 | -40+60 | -60+80 | -80+100 | -100+150 | -150+200 | -200 | -320 | |||||
(>425 m) | (250-425µ m) | (180-250 µ m) | (150-180 µ m) | (106-150 µ m) | (75-106 µ m) | (<75 µ m) | (<45 µ m) | |||||
32 | — | <1 | 5-20 | Balance | Balance | Balance | Balance | <20 | — |
HSM40·370
Fe | Mn | Si | C | S | P | Hydrogen loss | Insolubles in HCL | Mo | Bulk density g/cm³ | |||
Min ( wt%) | Max ( wt%) | |||||||||||
98.00 | 0.35 | 0.15 | 0.08~0.12 | 0.020 | 0.020 | 0.40 | — | — | 3.60~3.80 | |||
Fluidity | Copressibility | Size distribution (mesh) % | ||||||||||
+40 | -40+60 | -60+80 | -80+100 | -100+150 | -150+200 | -200 | -320 | |||||
(>425 m) | (250-425µ m) | (180-250 µ m) | (150-180 µ m) | (106-150 µ m) | (75-106 µ m) | (<75 µ m) | (<45 µ m) | |||||
30 | — | <1 | 5-45 | Balance | Balance | Balance | Balance | <20 | — |
More detailed SPC will be provided under request.
iron powder