Shaping-retentive carbon fiber composite is a new type of heat insulating material combining the PAN-based felt with graphite.

  Shaping-retentive carbon fiber composite is a new type of heat insulating material combining the PAN-based carbon felt with graphite paper by the special technology. Main characteristics: smooth surface, high compressive and bending strength, airflow abrasion resistance, fuzz resistance, without short fiber blowing and high anti-radiation. The shaping-retentive carbon fiber composite can take place various of imported heat insulating material in vacuum furnace and widely used in hot isostatic pressing furnace, pressure and high flow rate vacuum gas quenching furnace, vacuum cenmentating furnace. It is the upgrading products in the equipments of vacuum metallurgy, vacuum high temperature ceramic sintering, single crystal silicon etc. It is the most ideal thermal insulating material in domestic vacuum field

Technology Properties
BulkDensity: 0.23-0.35g/cm³ SpecificHeat: 0.17cal/g·k Carbon Content: ≥92%	Thermal Conductivity: 1500ºC: 0.15W/m·k 2000 (vacuum) ºC: 0.25 W/m·k
Compressive Strength: Parallel: 0.4-1.1MPa Vertical: 12-0.20MPa	Bending Strength: Parallel: 1.5-2.4MPa Vertical: 0.7-1.2MPa
Dimension	Usage Temperature
Plate Thickness: Min.:   20mm Max.:   150mm Cylinder: Max.Dia.:1300mm Max.Height:1600mm Min.Thickness:20mm	Oxidizing atmosphere: 300ºC In vacuum condition: 1800ºC Protective atmosphere: 2000ºC