1.easy flow 2.lopw cost ones 3.shows perfect performance in contact brazing 4.good wettabitity 5.higher strength ,

Pho-copper-silver and pho-copper brazing alloys are easy-flow ,low cost ones and shows perfect performance in contacting brazing ,oxy-acetylene  brazing, induction brazing and furnace brazing. the joint  strength  is higher  and conductivity is better. Flux is required while brazing brass to brass.  Pho-copper-silver alloys have good wettability, high strength and toughness of toughness of brazing seam and lower melting point. The heating speed should be as quick as possible while brazing.The joint is to be bright grey and will reture to the original color of bronze into 10% sulphuric acid.

Product Number	Related standard	Chemical Composition			Melting Range(°C)		Application
		Ag	P	Cu	Solidus	Liquidus
GWY-6P	L-CuP6	—	6.0	Bal.	710	890	Good capillary flow and ductility ,Capillary brazing of copper, brass and bronze , No flux is required for copper
GWY-7P	BCu93P	—	6.8-7.5	Bal.	710	790
	L-CuP7	—	7.0	Bal.	710	790
	BCuP-2	—	7.0-7.5	Bal.	710	793
GWY-8P	BCu92P	—	7.5-8.5	Bal.	710	793
	L-CuP8	—	8.0	Bal.	710	770
GWY-7PSn	L-CuSn7	Sn:6.8-7.2	6.6-7.0.	Bal.	650	700

Low-cost Phos-copper-silver 2B brazing round rod