Huayang aluminum is a aluminum profile manufactory, our main product is aluminum pipe.
The size 8~70mm,wall thickness is above 0.6,complete specification.
The product is mainly used in cleaning equipment (such as mopstick),machinery(such as mowing machine)and outdoor furniture(such as beach chair) and so on.
Our company use new aluminum ingot as raw material ,Don’t add any waste aluminum,Supplier provide spectral analysis report .
The company also equipped with advanced oxidation production line,Oxidation tank size : long 7.5 M, wide 1.3 M, deep 1.7 M
The colour of electrolytic oxidtion : bronze, K golden yellow,copy steel colour and black.Also we can do all kinds of dyeing oxidation: pink, blue, red ect.
Aluminum extrusion products
Material: Aluminium alloy 6063, 6061, 6005, etc.
Typical chemical composition (GB/T3190)
| Aluminum Grade | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | impurity | Al |
| 6063 | 0.2-0.6 | <0.35 | <0.1 | <0.1 | 0.45-0.9 | <0.1 | <0.1 | <0.1 | <0.15 | Rest |
| 6061 | 0.4-0.8 | 0.7 | 0.15-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | 0.25 | 0.15 | ≤0.15 | Rest |
| 6005 | 0.6-0.9 | 0.35 | <0.1 | <0.1 | 0.40-0.6 | <0.1 | <0.1 | <0.1 | <0.15 | Rest |
Temper: T5, T6, etc
6063-T5 aluminum extrusion.
T5 temper 6063 has an ultimate tensile strength of at least 22,000 psi (152 MPa) in thicknesses up to 0.5-inch (13 mm), and 21,000 psi (145 MPa) from 0.5 to 1.0-inch (25 mm) thick, and yield strength of at least 16,000 psi (110 MPa) up to 0.5-inch (13 mm) and 15,000 psi (103 MPa) (from 0.5 to 1.0-inch (25 mm). It has elongation of 8%.
6063-T6 aluminum extrusion
T6 temper 6063 has an ultimate tensile strength of at least 30,000 psi (207 MPa) and yield strength of at least 25,000 psi (172 MPa). In thicknesses of 0.124-inch (3.1 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.
6061-T6 aluminum extrusion
T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa).
Surface finish: Mill finish,Anodizing,Poder coated, Electrophoresis,etc.
"Mill Finish" is the natural appearnace of the aluminum as it comes from the rolling mill or the aluminum extrusion mill. Aluminum with mill finish has a very lightly oxidized film and will wipe off with your bare finger and immediately form.
"Anodizing" is an electrolytic passivation process used to increase the thickness of the natural oxide layer on the surface of aluminum extrusions, ranging may from 0.0003 inches thick on up to 0.003 and on up. Anodizing increases corrosion resistance and wear resistance, also can be used for a number of cosmetic effects.
"Powder coating" is a type of coating that is applied as a free-flowing, dry powder. The coating is typically applied electrostatically and is then cured under heat to allow it to flow and form a skin.
Other details.
| Dimensions | Max section: 250*250mm; Max length: 6.8 Meters | |||||||||
| Trade Term | FOB, CIF | |||||||||
| MOQ | 500 Kgs | |||||||||
| Drawings | Received, or provided by our engineers | |||||||||
| Dies | In-house fabricated (require 7-12 days) | |||||||||
| Further (deep) processing | Available,such as CNC machining, punching, drilling, tapping, welding | |||||||||
| Properties | Low weight with high strength, easy machining | |||||||||