LCD-A 01F
Product Type
100% biodegradable starch blend plastic resin
Film blowing type
Eco-friendly products
Product Properties
project | testing method | Testing condition | unite | standard |
density | ASTM D1505-03 | @23 °C | g/cm3 | 1.0-1.25 |
melt-mass flow rate | ASTM D1238 | @190 °C, 2.16kg | g/10 min | 1.0-3.0 |
tensile strength | ASTM D882 | 500mm/min | MPa | ≥15 |
breaking elongation | ASTM D882 | 500mm/min | % | ≥250 |
Bio-substance content | ASTM D6866 |
| % | ≥5 0 |
degradation rate | ASTM D6400 & EN13432 | in 180 days | % | ≥9 0 |
Procession Equipment
common film blowing machine equipments available
Procession Technology
a. the screw rotation should be slow at first ,and then adjust the screw rotation faster to match the request.b. fleshly blown film product feels a little brittle and crisp ,due to dehydration in production ,after 24 hours ,its function regains to normal plastics . c. the preferred blow-up ratio is 1:2.5, the height from die of orifice to the nip roll should be higher than 2.5m which to insure full cooling and prevent film blocking.d. using blowing temperature for referencephase | Phase I | Phase II | Phase III | Phase VI | Phase V |
Temperature( °C) | 125 | 140 | 140 | 145 | 140 |
100% biodegradable & compostable resin