1.High Hardness 2.Free Alkali glass bead 3.size: 0-40um, 40-60um, 60-90um, 70-100um 4.Used for grinding, blasting, polishing.

Blasting Glass  Beads with Non Alkali

1. The chemical composition is inert silicon dioxide, having no chemical activity and free from any interference;

2. Spherical particles can withstand impact resistance and can be recycled for many times with less wear and tear; 

3. Applying small amount to the sprayer will prolong the service life of the nozzle; 

4. After being treated, the product surface will be smooth and beautiful, which increases the product value; 

5. Suitable for dry and wet-type sandblasting operation; 

6. Metal micro-cracks can be easily revealed after being sandblasted with fine glass beads; 

7. The ball will not damage the machine surface and precision size; 

8. The processed product has lusterless effects and highlights the original metal color; it is rust-proof with no need for acid rust treatment; 

9. Non-Alkali glass microbead has higher hardness and the number of repeated use is much more than common micro-beads and the grain size can be much smaller, suitable for the polishing treatment of precision equipment. 

Purpose: 

1. Polish aviation parts, relieve stress to improve anti-fatigue strength and reduce friction and wear; 

2. Sandblasting for removing rust, paint, carbon deposition and machining marks; 

3. Pre-treatment before anodizing and plating to increase adhesive force besides cleaning; 

4. Clean the weld bead of stainless steel product and remove surface scratches; 

5. Clean and remove rust for wire-cutting die; 

6. Remove dirt for rubber die; 

Chemical Composition:

Program	SiO2	Al2O3	CaO	MgO	Na2O	K2O	B2O3	Fe2O3
HM-BEAD	72%	2.1%	7.0%	3.0%	13.8%	0.9%	--	0.2%
HE-BEAD	54%	14.6%	16.6%	4.6%	<0.5%	<0.3%	8.8%	<0.5%

Physical Specs

	HM-BEAD	HE-BEAD
Hardness1 (kgf/mm2)	425	540
Hardness2 (Mohs)	6.5	7.5
Abrasion (%)	3.14	1.96
Specific Gravity(20/20ºC)	2.52	2.62
Compressive Strength	16.64	21.51
Refractive Index	1.5-1.64	1.5-1.6
Specific Heat (cal/g ºC)	0.81	1.92
Thermal Conductivity (kcal/m.hr. ºC	0.65	--
Softening Point(ºC)	720	840
Thermal Expansion Coefficient  (ºC)	8.5×10-6	4×10-6
Resistance to weather	No change	No change

Note:  HE Bead means Non-Alkali glass microbead

      HM Bead means ordinary glass mircobead

Packing:

1.Using double-deck package, the inner is polythene film and its thickness is no less than 0.5mm, the outer is craft paper bag to prevent 

leak or damp. The net weight of each bag is 25±0.2kg. 

2. Per clients' requirement. 

High Indensity Blasting Glass Beads