CO2 welding wire 1.Diameter: 0.8-1.6mm; 2.Packing: 15/20kgs spools. 3,Good Quality,Best Price. 4,Welcome to our company.

CO2 welding wire WS-AS.18,ER70S-6   Dia:0.8-1.6

 suitable for thin plates

For AWS-AS.18,ER70S-6

FEATURE:Good project result and high quality weld can be obtained .The arc has stable burning and shallow penetration ,which is quite suitable for thin plates ,easy to operate.All position welding one side welding with back formation,beautiful oppearance of weld and no spatter.

Chemical composition of AWS ER70S-6 welding wire(%) 

C	Mn	Si	S	P	Cu
0.06~0.15	1.40~1.85	0.85~1.15	≤0.025	≤0.025	≤0.30

 

 

Metal mechanical property of welding seam

σb(MPa)	σs(MPa)	δ5 (%)	AKV(J)  -30°C
≥500	≥420	≥22	-29≥27

ER70S-6 welding wire

Er70s-6 Welding  Wire is a kind of welding technology developed in the 1950s. During the 40 years or so, it has been developed as a kind of important melt welding method and widely applied to all kinds of fields like automotive industry, construction machinery production, shipbuilding, metallurgical equipment production, bridges, civil works, petrochemical industry, production of pressure vessels of boilers, locomotive vehicles, etc.  

   At present, the production and application of CO2 gas-shielded welding wire have been developing rapidly. It has accounted for 40-50% in welding materials in some industrialized countries. In china, it has been popularized in many departments, and gradually it is partly replacing manual arc welding with electrodes gradually. Some of its characteristics are as follows,   1. Low welding costs.   2. High productivity and low electricity consumption.   3. Easy to operate. All-position welding.   4. Very low hydrogen content in the weld and lower nitrogen content. Excellent crack-resistance.   5. Little deformation after welding.   6. Wide applicability. Suitable for welding thin, medium and thick plates.

Introduction Strong resistance to surface scales and oil stains on the base metal. It has low blowhole sensitivity.

Uses: 1. Used for welding all kinds of 500MPa structural steel parts.2.Used for welding all kinds of 500MPa plates and pipes.

Chemical Composition of Welding Wire(%) C Mn Si S P Cu 0.06~0.15 1.4~1.85 0.8~1.15 ≤0.035 ≤0.025 ≤0.50

Examples of Chemical Composition of Deposited Metal (%) C Mn Si S P Cu 0.07 1.27 0.76 0.014 0.015 0.15

Mechanical Properties of Deposited Metal Test Item Rm(MPa) ReLRp0.2(Mpa) A(%) KV2(J) Guarantee Value ≥500 ≥420 ≥22 ≥27(-30) General Result 558 472 27 98

Reference Current (DC+) Wire Size(mm) Welding Current(A) CO2 Flow Rate(L/min) φ0.8  50~100  15  φ1.0  50~220  15~20 φ1.2  80~350  15~25 φ1.6  170~550                   Above Please Reference,any question Please contact us as following contACT INFORMATION