With reference to the technical requirements of Corning Incorporated, after several years of research and development, our company improved the existing technical equipment. We can produce diesel particulate filters with maximum diameter up to 330mm, with averge pore diameter of 10 ~ 12μm, and porosity close to that of the world's advanced level. We were the first in China to industrialize diesel particulate filters with “large diameter, multi-pores, high porosity”. Meanwhile, we’ve also undertaken a task in 2012 National Industry Promotion and Technological Transformation Special Fund Support Project to produce nitrogen and oxygen sensors and catalytic converter post-processing system used in medium and heavy-duty diesel vehicles.
Material Attributes:
Property (uncatalyzed) | 100/17 | 200/12 | |
Cell density | cpsi | 100 | 200 |
cpscm | 15.5 | 31.0 | |
Wall thickness | inch | 0.017 | 0.012 |
mm | 0.432 | 0.305 | |
Open frontal area (OFA), % | 34.5 | 34.5 | |
Geometric surface area (GSA) | Inch2 | 33.3 | 47.0 |
m2/l | 1.31 | 1.85 | |
Hydraulic diameter | Inch | 0.083 | 0.059 |
mm | 2.11 | 1.49 | |
Modulus of rupture (psi/cpscm) | 350 | 300 | |
Porosity (%) | 48 | 48 | |
Coefficient of thermal expansion 102 cm/cm/ (20-800) --maximum average | 5 | 5 | |
Mean pore size (micron) | 13 | 13 | |
Melting temperature () | 1460 | 1460 |
Physical components
Component | Unit | Data | Component | Unit | Data |
SiO2 | wt% | 48-51 | Fe2O3 | wt% | <0.5 |
Al2O3 | wt% | 31-34 | Na2O | wt% | <0.5 |
MgO | wt% | 14-16 | K2O | wt% | <0.5 |
Specifications:
100cpsi
NO. | Item | Our products | |
1 | Filter material | Cordierite and Silicon carbide | |
2 | Operating temperature limit (0C) | 1000 | |
3 | Dimension (mm) | Ø144x150,Ø144x152.4,Ø150x150,Ø190x200,Ø190x203, Ø240x240,Ø240x305 Ø260x305, Ø267x305, Ø286x305, Ø286x355,Ø374x270x317 | |
4 | Cell pitch (mm) | 100 cpsi | |
5 | Cell wall thickness (mm) | 0.45-0.52 | |
6 | Cell size (mm) | 2.02-2.09 | |
7 | Mean pore size (um) | 8-13 | |
8 | Porosity (gas pocket rate) % | 50-55 | |
9 | Coefficient of thermal expansion | 1.6x10-6 | |
10 | Softening temperature (0C) | 1360 | |
11 | Compressive Strength (Mpa) | Lengthwise direction | 10 |
Lateral direction | 2 | ||
12 | Water absorption rate: | 35% |